RIALFLAME H V0HF 15 S
PP(聚丙烯)
RIALTI
产品描述
Polyproplene homopolymer compound flame retardanted; classifiable, according to the norms of UL94, V0 up to 1.5mm. Totally halogen and heavy metals free, excellent properties of flame reaction with few emission of smoke at low density and opacity.
High flowability for injection molding in applications for the electric and electronic field. Available in natural version and colored as per sample.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤低烟浓度高流动均聚物 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.05 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 15 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.5 % | ISO 294-4 | |
横向(Across Flow) | 1.5 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 30 Mpa | ISO 527-2/50 | 23°C |
断裂(brk) | 21 Mpa | ISO 527-2/50 | 23°C |
拉伸延伸率 | |||
屈服(yld) | 3 % | ISO 527-2/50 | 23°C |
断裂(brk) | 21 % | ISO 527-2/50 | 23°C |
弯曲强度 | |||
- | 48 Mpa | ISO 178 | 23°C |
弯曲模量 | 2700 Mpa | ISO 178 | 23°C, 2.0 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 20 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 2.3 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 77 D | ISO 868 | 15 sec |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 62 °C | ISO 75-2/Af | Unannealed |
维卡软化温度(Vicat) | 95 °C | ISO 306/B50 | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
2mm | 960 °C | IEC 60695-2-12 | |
4mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
2.0mm | 775 °C | IEC 60695-2-13 |