Maxxam™ FR PP FR 7B31
PP(聚丙烯)
埃万特(原普立万)(Avient)
产品描述
Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击热稳定阻燃中粘度 | |||
| 添加助剂 | 阻燃剂热稳定剂 | |||
| 颜色形状 | 粒状 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
比重 | 0.93 - | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 5~10 g/10min | ASTM D 1238 | |
比容 | 1.08 cm³/g | ASTM D792 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 22.1 Mpa | ASTM D638 | Type I, 51 mm/min |
拉伸延伸率 | |||
断裂(brk) | 250 % | ASTM D638 | Type I, 51 mm/min |
弯曲模量 | 1050 Mpa | ASTM D790 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 640 J/m | ASTM D256 | 3.18 mm, Injection Molded |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 73 °C | ASTM D648 | Unannealed, 3.18 mm |
相对温度指数(RTI) | |||
冲击w/impact,1.5/1.6 mm | 105 °C | UL 746 | |
冲击w/impact,3.0/3.2 mm | 105 °C | UL 746 | |
电气Elec,1.5/1.6 mm | 105 °C | UL 746 | |
电气Elec,3.0/3.2 mm | 105 °C | UL 746 | |
强度w/o impact,1.5/1.6 mm | 105 °C | UL 746 | |
强度w/o impact,3.0/3.2 mm | 105 °C | UL 746 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-2 | 1.5 mm | UL94 | |
V-2 | 3 mm | UL94 | |
V-2 | 0.75 mm | UL94 | ALL |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+16 Ohm-cm | ASTM D257 | |
相比漏电起痕指数(CTI ) | |||
- | 0 PLC | UL 746 | |
绝缘强度 | 26 kV/mm | ASTM D149 | |
高电压电弧起痕速率(HVTR) | 0 PLC | UL 746 | |
热线圈起燃性(HWI) | 3 PLC | UL 746 | 0.75 mm |
热线圈起燃性(HWI) | 3 PLC | UL 746 | 1.5 mm |
热线圈起燃性(HWI) | 2 PLC | UL 746 | 3.0 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | 0.75 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | 1.5 mm |
高电流弧起燃性(HAI) | 0 PLC | UL 746 | 3.0 mm |