Daplen™ EE108U
PP(聚丙烯)
博禄/北欧化工(Borealis AG/Borouge)
产品描述
Daplen EE108U is a 10% mineral filled elastomer modified polypropylene compound intended for injection moulding.
This material has an excellent balance between impact strength and stiffness, gives a good surface quality and is easy to process.
Applications
Daplen EE108U has been developed especially for applications like: Body side mouldings Bumpers Exterior trims
Special features
UV stabilised High flowability allowing to mould complex-structured parts with very high "flow path / wall thickness ratios" Excellent Scratch resistant Excellent surface appearance on unpainted and grained parts
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 良好的刚性良好冲击性良好表面耐刮擦易成型抗紫外线高流动填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 10% 矿物弹性体 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.99 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 16 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.9 % | Internal | Mould average Shrinkage (disk) |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 16 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-2 | 50 mm/min |
断裂(brk) | 100 % | ISO 527-2 | 50 mm/min |
弯曲强度 | |||
- | 20 Mpa | ISO 178 | |
弯曲模量 | 1100 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 1000 Mpa | ISO 527-2 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | |
-20℃ (-4℉) | 7 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 35 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-20℃ (-4℉) | NB kJ/m² | ISO 179/1eU | |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 5 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 37 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 31 Mpa | ISO 2039-1 | 132 N/10 s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 85 °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 51 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 115 °C | ISO 306 | 10 N |
维卡软化温度(Vicat) | 42 °C | ISO 306 | 50 N |
线性膨胀系数(CLTE) | |||
- | 61 E-6/K | Internal | -30 °C/80 °C |