Finalloy® SR-64N S11
PP(聚丙烯)
道达尔能源(Total Energies)
产品描述
Finalloy SR-64N S11 a 15% mineral-filled and impact-modified polypropylene-based compound that combines a good impact/rigidity balance with very good processability.
Finalloy SR-64N S11 in-coloured compounds are particularly suitable for the injection moulding of non-painted, visible automotive interior parts that require an excellent scratch resistance. The surface of parts produced with this material will not become sticky after exposure to heat and uv light.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性热稳定耐刮擦易成型抗紫外线填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 成型方式 | 注塑 | |||
| 应用产品 | 汽车内饰件 | |||
| 增强填充 | 15% 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 25 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.85~1.15 % | Internal | t=3mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 21 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527 | |
断裂(brk) | 50 % | ISO 527 | |
弯曲模量 | 1800 Mpa | ISO 178 | |
拉伸模量 | 1650 Mpa | ISO 527 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
-20℃ (-4℉) | 5 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 25 kJ/m² | ISO 179/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 64 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 110 °C | ISO 75-2 | 120°C per hour |
维卡软化温度(Vicat) | 135 °C | ISO 306/A50 | 10N, 50°C/h |
线性膨胀系数(CLTE) | |||
- | 75 E-6/K | ISO 11359-2 | |
熔融温度(Tm) | 160~165 °C | Internal |