SABIC® PPCOMPOUND 8511E
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC® PPcompound 8511E is a mineral filled elastomer-modified polypropylene for automotive painted bumper and painted exterior cladding applications. The material combines good flow with high impact, stiffness and low CLTE. The stiffness level of this material is such that thin wall applications are possible. This grade is emission optimized.
SABIC® PPcompound 8511E is a designated automotive grade.
IMDS ID:
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性高冲击增韧/冲击改性低收缩低线性膨胀易涂装低挥发VOC填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 增强填充 | 20% 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.035 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 26 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.7 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527/1A | |
断裂(brk) | 15 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 12 % | ISO 527/1A | |
弯曲模量 | 2200 Mpa | ISO 178/1A | |
拉伸模量 | 1850 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 6 kJ/m² | ISO 180/1A | |
0℃ (32℉) | 9 kJ/m² | ISO 180/1A | |
23℃ (73℉) | NB kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 110 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 59 °C | ISO 75/A | |
线性膨胀系数(CLTE) | |||
- | 70 E-6/K | ISO 11359-2 | -30 °C to 100 °C |