Moplen HP525J
PP(聚丙烯)
利安德巴塞尔(LyondellBasell)
产品描述
Moplen HP525J is a polypropylene homopolymer designed for the production of biaxially oriented polypropylene films (BOPP). The product is suitable for metallizable film, both as monolayer and in coextruded structures. It contains a standard processing stabilisation but does not contain any slip, antiblocking agents and no Calcium Stearate is intentionally added. Moplen HP525J offers good optical, easy processing and very good film profile. Typical applications are BOPP packaging films and Solid Phase Thermoforming sheets.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 良好光学性高光泽易成型中粘度均聚物 | |||
| 成型方式 | BOPP | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.9 g/cm³ | ISO 1183 | |
密度 | 0.9 g/cm³ | ASTM D792 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 3 g/10min | ASTM D 1238 | |
230°C/2.16 kg | 3 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33 Mpa | ASTM D638 | |
屈服(yld) | 34 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 23 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 11 % | ASTM D638 | |
屈服(yld) | 12 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 500 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
弯曲模量 | 1500 Mpa | ASTM D790 | |
弯曲模量 | 1450 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 34 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 70 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 97 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） | 85 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 154 °C | ISO 306/A50 |