产品描述
PRE-ELEC® PP 18900 is electrically conductive thermoplastic concentrate based on polypropylene. Conductivity is achieved by using special conductive carbon black. It contains a high load of carbon black and it can be diluted with virgin or recycled PP. The actual amount should always be tested as it also depends on the processing conditions.
The values with the exception of MFR are measured from dilution: 30% PP-C, MFI 13 ( 230°C/2.16 kg)
基本信息
原厂资料 | 物性表(英文) PRE-ELEC牌号选择 | |||
产品特性 | 导电母粒 | |||
成型方式 | 挤出共混改性 | |||
增强填充 | 炭黑 |
技术参数
物理性能 | 值/单位 | 测试标准 | 测试条件 |
---|---|---|---|
密度 | 1.06 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/5 kg | 0.5 g/10 min | ISO 1133 | |
收缩率 | |||
- | 1.3~1.6 % | ISO 294-4 | |
机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 20 Mpa | ISO 527 | extruded tape; Thickness 600-800 µm |
拉伸延伸率 | |||
断裂(brk) | 15 % | ISO 527 | extruded tape; Thickness 600-800 µm |
弯曲模量 | 1500 Mpa | ISO 178 | |
冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 6 kJ/m² | ISO 179 | |
23℃ (73℉) | 8 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
-20℃ (-4℉) | NB kJ/m² | ISO 179 | |
23℃ (73℉) | NB kJ/m² | ISO 179 | |
硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 90 A | ISO 868 | |
邵氏硬度 D | 71 D | ISO 868 | |
热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)(4.6kg/cm²) | 87 °C | ISO 75/Bf | |
1.8 Mpa (264 psi)(18.6kg/cm²) | 53 °C | ISO 75/Af | |
维卡软化温度(Vicat) | 86 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 152 °C | ISO 306/A50 | |
电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 4E+0 Ohm-cm | Internal | extruded tape; Thickness 600-800 µm |
表面电阻率 | 6E+2 Ohm | IEC 61340-2-3 | extruded tape; Thickness 600-800 µm |