POLIMAXX 2500H
PP(聚丙烯)
泰国石化(IRPC)
产品描述
2500H is a Polypropylene Impact Copolymer (ICPP) with the characteristic of super high impact strength (Not Break). It is designed for extrusion processing such as sheet thermoforming (Tray, cup, corrugated sheet), automotive parts (Exterior and interior parts).
INDUSTRY
-Automotive Parts
-Exterior & Interior Parts
-Thermoforming Packaging
-Extrusion Blow Molding (EBM)
-Stationery
PRODUCT FEATURE
-Super High Impact Strength
-Good Processability
REGULATION COMPLIANCE
-FDA US 21 CFR 177.1520
-Commission Regulation(EU) No. 10/2011
-RoHS Directive 2011/65/EU
-REACH Regulation (EC) No. 1907/2006
-Halal Certificate
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击易成型食品接触级 | |||
| 成型方式 | 挤出挤出吹塑热成型 | |||
| 应用产品 | 托盘薄板杯子汽车零部件文具波纹板 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.9 g/cm³ | ASTM D792 | 23°C |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 2 g/10min | ASTM D 1238 | |
收缩率 | |||
- | 0.8~1.5 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 25 Mpa | ASTM D638 | 3.2 mm, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ASTM D638 | 3.2 mm, 50 mm/min |
弯曲模量 | 1100 Mpa | ASTM D790 | 1% Secant, 3.2 mm, 1.3 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 95 J/m | ASTM D256 | 3.2 mm |
23℃ (73℉) | NB J/m | ASTM D256 | 3.2 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 78 R | ASTM D785 | 3.2 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 92 °C | ASTM D648 | Unannealed, 3.2 mm |
原材料现货供应:133-8218-6680(微信同号)