RIALFLAME H V0HF 07 S 30 G
PP(聚丙烯)
RIALTI
产品描述
Self-extinguishing, classifiable V0 according to the norms of the Underwriters Laboratories Inc.(UL-94). Totally halogen and heavy metals free, excellent properties of flame reaction with few emission of smokes at low density and opacity. Flowability for injection molding in applications for the electric and electronic field. Available in natural version and coloured as per sample.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤低烟浓度均聚物填充增强含回收料 | |||
| 添加助剂 | 阻燃剂 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.27 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 3 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.35 % | ISO 294-4 | |
横向(Across Flow) | 1.8 % | ISO 294-4 | |
填充/灰分 | 30 % | ISO 3451 | |
回收料含量(PCR) | 70 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 65 Mpa | ISO 527-2/50 | 23°C |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ISO 527-2/50 | 23°C |
弯曲强度 | |||
- | 110 Mpa | ISO 178 | 23°C |
弯曲模量 | 8000 Mpa | ISO 178 | 23°C, 2.0 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 25 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 140 °C | ISO 75-2/Af | Unannealed |
维卡软化温度(Vicat) | 130 °C | ISO 306/B50 | |
球压痕温度 | 125 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
V-0 | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1mm | 850 °C | IEC 60695-2-12 | |
2mm | 850 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
1.0mm | 775 °C | IEC 60695-2-13 | |
2.0mm | 775 °C | IEC 60695-2-13 |