Total Energies Polypropylene PPC 9712
PP(聚丙烯)
道达尔能源(Total Energies)
产品描述
Polypropylene PPC 9712 is heterophasic copolymer with a Melt Flow Index of 25g/10 min combining good fluidity and mechanical properties.
Polypropylene PPC 9712 is characterized by excellent impact resistance and antistatic properties and has been formulated to allow faster cycling through early demoulding.
Polypropylene PPC 9712 has been developed specifically for the injection moulding of crates, pails and other heavy duty applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好冲击性抗静电 ESD短周期成型易脱模食品接触级成核的 | |||
| 添加助剂 | 抗静电剂成核剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 25 g/10min | ISO 1133 | |
堆积(视)密度 | 0.525 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 23 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2 | |
弯曲模量 | 1050 Mpa | ISO 178 | |
拉伸模量 | 1150 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 6 kJ/m² | ISO 179 | |
23℃ (73℉) | 40 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 5.5 kJ/m² | ISO 180 | |
23℃ (73℉) | 40 kJ/m² | ISO 180 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 80 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 90 °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | 48 °C | ISO 75 | 120°C per hour |
维卡软化温度(Vicat) | 135 °C | ISO 306 | 10N-50°C per hour |
维卡软化温度(Vicat) | 65 °C | ISO 306 | 50N-50°C per hour |
熔融温度(Tm) | 165 °C | ISO 3146 |