Borealis TR503T
PP(聚丙烯)
博禄/北欧化工(Borealis AG/Borouge)
产品描述
TR503T This grade is characterized by excellent impact strength even at low temperatures combined with high stiffness and good flow properties. is a 10% mineral filled polypropylene compound intended for injection moulding. is a polypropylene homopolymer intended for injection moulding.
Applications
TR503T has been developed especially for the automotive industry. Bumpers
Special Features
impact strength at low temperature
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高刚性良好冲击性耐低温冲击良好流动性均聚物填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 10% 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.965 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 13 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 17 Mpa | ISO 527-2 | 50 mm/min |
弯曲强度 | |||
- | 22 Mpa | ISO 178 | |
弯曲模量 | 1100 Mpa | ISO 178 | 2 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 5 kJ/m² | ISO 180/1A | |
0℃ (32℉) | 15 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 35 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 85 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ISO 75-2 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
燃烧速率 | 100 mm/min | ISO 3795 | thickness 1 mm |