Metocene HM562S
PP(聚丙烯)
利安德巴塞尔(LyondellBasell)
产品描述
Metocene HM562S is a metallocene-catalysed polymer with a very narrow Molecular Weight Distribution, suitable for extrusion application. It is formulated with an anti-gas fading stabilization package. It can be advantageously processed in different spinning technologies. Typical applications are spunbond nonwovens and continuous filaments such as partially-oriented yarns (POY). Metocene HM562S expands processing capabilities to achieve unmatched properties balances. It allows faster spinning and lower denier filaments. Additional advantages of Metocene HM562S are low volatiles and processing smokes.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 均聚物 | |||
| 成型方式 | 挤出纺纱/丝 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
熔体体积流动速率(MVR) | |||
230℃/2.16 kg | 40 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 30 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 31 Mpa | ISO 527-1/-2 | 23 °C |
拉伸延伸率 | |||
屈服(yld) | 10 % | ISO 527-1/-2 | 23 °C |
断裂(brk) | 50 % | ISO 527-1/-2 | 23 °C |
弯曲模量 | 1400 Mpa | ISO 178 | 23 °C |
拉伸模量 | 1450 Mpa | ISO 527-1/-2 | 23 °C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 3 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 93 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 82 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 136 °C | ISO 306/A50 | |
熔融温度(Tm) | 145 °C | ISO 3146 |