PRE-ELEC® PP 1384
PP(聚丙烯)
普宓斯(PREMIX)
产品描述
PRE-ELEC® PP 1384 is a conductive thermoplastic compound based on polypropylene. Conductivity is achieved by using special conductive carbon black. In addition to a low electrical resistivity PRE-ELEC® PP 1384 has excellent mechanical properties and is easy to extrude.
PRE-ELEC® PP 1384 is recommended to be used in polypropylene tape co-extrusion for FIBC (type C) applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 导电 | |||
| 成型方式 | 挤出 | |||
| 增强填充 | 炭黑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.06 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 1 g/10min | ISO 1133 | |
230°C/5 kg | 16 g/10 min | ISO 1133 | |
收缩率 | |||
- | 1.2~1.7 % | ISO 294-4 | 4.0 mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
弯曲模量 | 2500 Mpa | ISO 178 | 4.0 mm |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 2 kJ/m² | ISO 179 | 4.0 mm |
23℃ (73℉) | 4 kJ/m² | ISO 179 | 4.0 mm |
简支梁无缺口(Charpy Unnotched) | |||
-20℃ (-4℉) | 5 kJ/m² | ISO 179 | 4.0 mm |
23℃ (73℉) | 14 kJ/m² | ISO 179 | 4.0 mm |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 1.2 kJ/m² | ISO 180 | 4.0 mm |
23℃ (73℉) | 1.5 kJ/m² | ISO 180 | 4.0 mm |
悬臂梁无缺口(Izod Unnotched) | |||
-20℃ (-4℉) | 9 kJ/m² | ISO 180 | 4.0 mm |
23℃ (73℉) | 16 kJ/m² | ISO 180 | 4.0 mm |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 A | 98 A | ISO 868 | 4.0 mm |
邵氏硬度 D | 73 D | ISO 868 | 4.0 mm |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 109 °C | ISO 75/Bf | 4.0 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 63 °C | ISO 75/Af | 4.0 mm |
维卡软化温度(Vicat) | 154 °C | ISO 306/A50 | 4.0 mm |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+1 Ohm-cm | Internal | 400µm |
表面电阻率 | 1E+2 Ohm | IEC 61340-2-3 | 400µm |
| 薄膜性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
- | 30 Mpa | ISO 527 | Flow, 400µm |
拉伸延伸率 | |||
断裂(brk) | 4 % | ISO 527 | Flow, 400µm |