SABIC® PPCOMPOUND H1030
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC®PPcompound H1030 is a good flow, halogen free flame retardant, homopolymer with 30% glass fiber, developed for E&E and automotive injection molded applications. It has a UL94V0@1.5mm and 5VA@3.0mm flame rating. This material has been designed to combine a good performance profile with good processing and FR characteristics.
IMDS ID: 712120555
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 阻燃无卤易成型良好流动性均聚物填充增强 | |||
| 添加助剂 | 阻燃剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.27 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 8 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.75 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 100 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527/1A | |
弯曲模量 | 8400 Mpa | ISO 178/1A | |
拉伸模量 | 8700 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 8 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 160 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 148 °C | ISO 75/A | |
球压痕温度 | 135 °C | IEC 60695-10-2 | PASS |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | UL94 | |
5VA | 3 mm | UL94 | |
灼热丝可燃性指数(GWFI) | |||
1.6mm | 960 °C | IEC 60695-2-12 | |
灼热丝点燃温度(GWIT) | |||
0.8mm | 825 °C | IEC 60695-2-13 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 |