Polypropylene PPH 1060 is a homopolymer with a high molecular weight and a Melt Flow Index of 0.3 g/10 min.
Polypropylene PPH 1060 is specifically designed for the extrusion of mineral modified pipes. It is also suitable for the extrusion of sheets and other technical parts.
The resin has a high temperature stabilization package. It offers a very high stiffness and a high heat distortion temperature.
Polypropylene PPH 1060 is available in natural color.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热食品接触级饮用水级 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 挤出片材挤出管材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 0.3 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 33 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-2 | |
弯曲模量 | 1500 Mpa | ISO 178 | |
拉伸模量 | 1600 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 8 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 7 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 100 °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | 55 °C | ISO 75 | 120°C per hour |
维卡软化温度(Vicat) | 152 °C | ISO 306 | 10N-50°C per hour |
维卡软化温度(Vicat) | 87 °C | ISO 306 | 50N-50°C per hour |
熔融温度(Tm) | 165 °C | ISO 3146 |