Finalloy® EBP-15X6H UC9B9
PP(聚丙烯)
道达尔能源(Total Energies)
产品描述
Finalloy EBP-15X6H UC9B9 is a mineral-filled and impact modified polypropylene-based compound that has a very low linear thermal expansion in combination with high modulus, good processability, good scratch resistance and reduced tiger marks. It has a high thermal stability.
Finalloy EBP-15X6H UC9B9 is UV stabilized and optimized for good surface aspect. It is particularly suitable for the injection moulding of unpainted automotive exterior parts like rocker panels, wheel arches, door trim lists and other parts which require low thermal expansion.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性良好表面耐刮擦低线性膨胀易成型抗紫外线填充增强 | |||
| 添加助剂 | 紫外线稳定剂抗冲击剂 | |||
| 成型方式 | 注塑 | |||
| 应用产品 | 汽车外饰件汽车侧裙板汽车轮拱车门内饰板 | |||
| 增强填充 | 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.12 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 20 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.4~0.65 % | Internal | t=3mm |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 18 Mpa | ISO 527 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527 | |
断裂(brk) | 30 % | ISO 527 | |
弯曲模量 | 2000 Mpa | ISO 178 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 3 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 18 kJ/m² | ISO 179/1eA | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 65 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 100 °C | ISO 75-2 | 120°C per hour |
维卡软化温度(Vicat) | 125 °C | ISO 306/A50 | 10N, 50°C/h |
线性膨胀系数(CLTE) | |||
- | 37 E-6/K | ISO 11359-2 | |
熔融温度(Tm) | 160~165 °C | Internal |