Borcoat™ EB133E-1199-LT
PP(聚丙烯)
博禄/北欧化工(Borealis AG/Borouge)
产品描述
Borcoat EB133E-1199-LT is an elastomer modified compound, based on a polypropylene copolymer.
It has excellent low temperature impact resistance.
The product is coloured white. It includes a combination of stabilisers to ensure long-term thermal stability.
The product is supplied in pellet form.
Applications
Borcoat EB133E-1199-LT is recommended as a top coat for multilayer PP systems and thermal insulation used in: Steel Pipe Coating
Specifications
Borcoat EB133E-1199-LT is intended to fulfil following National and International standards, when appropriate industrial manufacturing standard procedures are applied and a continuous quality system is implemented and when used in combination with Borcoat™ BB122E-LT and a compatible powder epoxy. ISO 21809-1 DIN 30678 NF A49-711 Gazprom 2-2.2-178-2007
Due to the nature of the modified PP material, indentation resistance of the applied coating could be borderline versus some requirements of common standards and due to known variations in testing, those specified values should be separately agreed upon between the applicator and the client (end user/purchaser).
Special Features
Borcoat EB133E-1199-LT is intended for design temperatures between -20°C and +110°C and tailored for low temperature handling, transportation and installation.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐低温冲击增韧/冲击改性热稳定 | |||
| 颜色形状 | 粒状白色 | |||
| 成型方式 | 挤出 | |||
| 增强填充 | 弹性体 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.915 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 1.2 g/10min | ISO 1133 | |
环境应力开裂(ESCR ) | 5000 Hours | ASTM D 1693 | 50 °C, Igepal 10 %, F50 |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 22 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 13 % | ISO 527-2 | 50 mm/min |
断裂(brk) | 400 % | ISO 527-2 | 50 mm/min |
拉伸模量 | 1000 Mpa | ISO 527-2 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179 | |
-20℃ (-4℉) | 5 kJ/m² | ISO 179 | |
23℃ (73℉) | 60 kJ/m² | ISO 179 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 60 D | ISO 868 | 1 s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 135 °C | ISO 306/A50 | 10 N |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
氧化诱导期(OIT) | 40 Min | ISO 11357 | 220 °C |