SABIC® PPcompound F9005 is an elastomer-modified mineral filled Polypropylene for automotive interior applications. This material has been designed to combine a good performance profile with good processing. This material is designed for intended use in foamed interior applications. Datasheet values are based on standard, solid specimen.
SABIC® PPcompound F9005 is a designated automotive grade.
IMDS ID: 963559648
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 增韧/冲击改性易成型可发泡填充增强 | |||
| 添加助剂 | 抗冲击剂 | |||
| 增强填充 | 5% 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.93 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 17 g/10min | ISO 1133 | |
收缩率 | |||
- | 1.4 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 22 Mpa | ISO 527/1A | |
断裂(brk) | 16 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 8 % | ISO 527/1A | |
弯曲模量 | 1400 Mpa | ISO 178/1A | |
拉伸模量 | 1400 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
0℃ (32℉) | 9 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 15 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 94 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 54 °C | ISO 75/A | |
线性膨胀系数(CLTE) | |||
- | 130 E-6/K | ISO 11359-2 | -30 °C to 100 °C |