Total Energies Polypropylene PPC 4663
PP(聚丙烯)
道达尔能源(Total Energies)
产品描述
Polypropylene PPC 4663 is heterophasic copolymer with a Melt Flow Index of 3.5 g/10min.
Polypropylene PPC 4663 is characterized by a combination of ease of processing and good manufactured article properties in applications ranging from household to industrial. These include the manufacture of chair shells, pails, crates and other articles requiring a combination of good stiffness and impact properties.
Polypropylene PPC 4663 has been formulated to give good UV resistance.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性良好冲击性易成型抗紫外线 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 3.5 g/10min | ISO 1133 | |
堆积(视)密度 | 0.525 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 25 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-2 | |
弯曲模量 | 1200 Mpa | ISO 178 | |
拉伸模量 | 1300 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 7 kJ/m² | ISO 179 | |
23℃ (73℉) | 20 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 5.5 kJ/m² | ISO 180 | |
23℃ (73℉) | 18 kJ/m² | ISO 180 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 82 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 92 °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | 50 °C | ISO 75 | 120°C per hour |
维卡软化温度(Vicat) | 147 °C | ISO 306 | 10N-50°C per hour |
维卡软化温度(Vicat) | 70 °C | ISO 306 | 50N-50°C per hour |
熔融温度(Tm) | 165 °C | ISO 3146 |