Hostacom PC072-3 natural
PP(聚丙烯)
利安德巴塞尔(LyondellBasell)
产品描述
30% glass coupled PP- homopolymer. Low flow, high stiffness, low CLTE and outstanding LTHA values. Low creep under load at elevated temperatures. The product is designed for injection molding of washing machine parts and is available in natural color. Good hot water and detergent resistance. UL listing in all colors including RTI and compliance with UL 2157. It is not intended for medical, pharmaceutical and drinking water applications.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高刚性热稳定耐热老化低线性膨胀抗蠕变耐水解耐洗涤剂高粘度均聚物填充增强 | |||
| 添加助剂 | 化学偶联剂 | |||
| 法规认证 | UL 2157(洗衣机与脱水机标准) | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.14 g/cm³ | ISO 1183 | |
比重 | 1.14 - | ASTM D792 | 23°C |
熔体体积流动速率(MVR) | |||
230°C/5.0 kg | 8 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 2 g/10min | ASTM D 1238 | |
230°C/2.16 kg | 2 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.3~1 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 90 Mpa | ASTM D638 | |
屈服(yld) | 85 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 80 Mpa | ISO 527-1/-2 | 50 mm/min |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | |
断裂(brk) | 3.5 % | ISO 527-1/-2 | 50 mm/min |
弯曲强度 | |||
- | 110 Mpa | ISO 178 | |
弯曲模量 | 6000 Mpa | ASTM D790 | |
弯曲模量 | 5400 Mpa | ISO 178 | Secant |
拉伸模量 | 6400 Mpa | ISO 527-1/-2 | Secant |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 6 kJ/m² | ISO 179 | Type 1, Edgewise, Notch A |
23℃ (73℉) | 9.5 kJ/m² | ISO 179 | Type 1, Edgewise, Notch A |
简支梁无缺口(Charpy Unnotched) | |||
-20℃ (-4℉) | 35 kJ/m² | ISO 179 | Type 1, Edgewise |
23℃ (73℉) | 40 kJ/m² | ISO 179 | Type 1, Edgewise |
悬臂梁缺口(Izod Notched) | |||
0℃ (32℉) | 85 J/m | ASTM D256 | |
23℃ (73℉) | 100 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 115 Mpa | ISO 2039-1 | H 358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 148 °C | ASTM D648 | Unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 155 °C | ISO 75-1/-2 | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 130 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 130 °C | ISO 306/B50 | B50 (50°C/h 50N) |
维卡软化温度(Vicat) | 160 °C | ISO 306/A50 | A50 (50°C/h 10N) |
相对温度指数(RTI) | |||
冲击w/impact,- | 105 °C | UL 746 | |
电气Elec,- | 105 °C | UL 746 | |
强度w/o impact,- | 105 °C | UL 746 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 |