SABIC® PP CX02-82
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC PP CX02-82 is an emission optimised high crystalline copolymer. It offers high stiffness, in perfect balance with high thermal dimensional stability, impact resistance and flow.
This material has excellent aesthetic properties as well and is typically used for automotive interior applications. It is the obvious alternative to conventional talc-filled copolymers, offering considerable weight saving advantage.
SABIC PP CX02-82 is a designated automotive grade.
IMDS ID: 80775790
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性高冲击热稳定低挥发VOC抗紫外线高流动共聚物成核的 | |||
| 添加助剂 | 紫外线稳定剂成核剂 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 15 g/10min | ISO 1133 | |
收缩率 | |||
- | 1.6 % | Internal | 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 27 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 4 % | ISO 527-2 | |
拉伸模量 | 1550 Mpa | ISO 527-2 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
0℃ (32℉) | 8 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 12.5 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 6 kJ/m² | ISO 180/1A | |
0℃ (32℉) | 7 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 11 kJ/m² | ISO 180/1A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 65 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
维卡软化温度(Vicat) | 80 °C | ISO 306/B | 120°C/h, at 50 N (VST/B) |
维卡软化温度(Vicat) | 151 °C | ISO 306/A | 120°C/h, at 10 N (VST/A) |
| 其他性能 | 值/单位 | 测试标准 | 测试条件 |
VOC挥发 | 50 µgC/g | VDA 277 |
原材料现货供应:133-8218-6680(微信同号)