Clyrell EC2458
PP(聚丙烯)
利安德巴塞尔(LyondellBasell)
产品描述
Clyrell EC2458 is a clarified polyolefinic resin combining the typical advantages of polypropylene random and heterophasic copolymers and is designed for injection moulding applications.
Clyrell EC2458 offers a good flowability with very high impact resistance at room and sub-zero temperatures, good transparency and good resistance to stress whitening.
Clyrell EC2458 can be processed at significantly lower temperatures which enable energy savings and improved productivity due to reduced cycle times.
Clyrell EC2458 is a developmental grade.
The main applications of Clyrell EC2458 are the production of clear containers with very high impact resistance for deep-freezer storage conditions.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高冲击耐低温冲击短周期成型高流动 | |||
| 颜色形状 | 透明 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.9 g/cm³ | ISO 1183 | |
比重 | 0.902 g/cm³ | ASTM D792 | |
熔体体积流动速率(MVR) | |||
230℃/2.16 kg | 40.5 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 30 g/10min | ASTM D 1238 | |
230°C/2.16 kg | 30 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527-1/-2 | |
断裂(brk) | 50 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 18 % | ISO 527-1/-2 | |
拉伸模量 | 850 Mpa | ISO 527-1/-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 4 kJ/m² | ISO 179 | Type 1, Edgewise, Notch A |
0℃ (32℉) | 6 kJ/m² | ISO 179 | Type 1, Edgewise, Notch A |
23℃ (73℉) | 20 kJ/m² | ISO 179 | Type 1, Edgewise, Notch A |
韧脆转变温度(DBTT) | -50 °C | ISO 6603-2 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 28 Mpa | ISO 2039-1 | H358/30 |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 60 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 52 °C | ISO 306/B50 | |
维卡软化温度(Vicat) | 114 °C | ISO 306/A50 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 20 % | ASTM D1003 | 1 mm |