SABIC® PPCOMPOUND 3310H
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC® PPcompound 3310H is a 10% talc filled grade which is high heat stabilized, developed for under the bonnet applications. This material has been designed to combine a good performance profile with good processing.
SABIC® PPcompound 3310H is a designated automotive grade.
IMDS ID: 663980321
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 增强填充 | 10% 滑石粉 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.97 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 25 g/10min | ISO 1133 | |
收缩率 | |||
- | 1.2 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 35 Mpa | ISO 527/1A | |
断裂(brk) | 35 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 14 % | ISO 527/1A | |
弯曲模量 | 2400 Mpa | ISO 178/1A | |
拉伸模量 | 2300 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 3 kJ/m² | ISO 180/1A |