SABIC® PPCOMPOUND 8578U
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC® PPcompound 8578U is an elastomer-modified mineral filled Polypropylene. This material shows good balance of processing and excellent performance profile. The grade is UV stabilized and has very good impact performance at low temperature. The material suited for use in large exterior unpainted applications.
SABIC® PPcompound 8578U is a designated automotive grade.
IMDS ID: 1052498885
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击增韧/冲击改性抗紫外线填充增强 | |||
| 添加助剂 | 紫外线稳定剂抗冲击剂 | |||
| 增强填充 | 12% 矿物弹性体 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.98 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 23 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.8 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 13 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 65 % | ISO 527/1A | |
弯曲模量 | 1500 Mpa | ISO 178/1A | |
拉伸模量 | 1450 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 9 kJ/m² | ISO 180/1A | |
0℃ (32℉) | NB kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 95 °C | ISO 75/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 52 °C | ISO 75/A | |
线性膨胀系数(CLTE) | |||
- | 90 E-6/K | ISO 11359-2 | -30 °C to 100 °C |