Moplen HP422H
PP(聚丙烯)
利安德巴塞尔(LyondellBasell)
产品描述
Moplen HP422H is a modified polypropylene homopolymer designed for the production of BOPP films at very high speed. BOPP films produced with HP422H feature good mechanical properties, excellent barrier against moisture, odours, oxygen, good transparency and gloss. Coextruded films made of Moplen HP422H are widely used in the food packaging industry. Moplen HP422H does not contain any slip or antistatic agents and no Calcium Stearate is intentionally added.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高光泽低气味均聚物高阻隔性 | |||
| 颜色形状 | 透明 | |||
| 成型方式 | BOPP | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.9 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 2 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 34 Mpa | ISO 527-1/-2 | 23 °C, 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 10 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
断裂(brk) | 410 % | ISO 527-1/-2 | 23 °C, 50 mm/min |
弯曲模量 | 1450 Mpa | ISO 178 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 70 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 88 °C | ISO 75-1/-2 | Unannealed |
维卡软化温度(Vicat) | 152 °C | ISO 306/A50 | |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
雾度 | 0.5 % | ASTM D1003 |