Borealis RA130E-8427 (industrial)
PP(聚丙烯)
博禄/北欧化工(Borealis AG/Borouge)
产品描述
RA130E-8427 (industrial) is a high molecular weight, low melt flow rate polypropylene random copolymer (PP-R) compound and is grey coloured.
Applications
RA130E-8427 (industrial) is recommended for the production of PP-R pipes and fittings used in below applications. For Plumbing & Heating and other applications please see seperate datasheet. Industrial applications
Specifications
RA130E-8427 (industrial) is intended to fulfill following standards and regulations, in case of appropriate industrial manufacturing standard procedures applied and a continuous quality system is implemented. DIN 8078 DIN 8077 EN ISO 15494
Special features
RA130E-8427 (industrial) is a ready made compound in pellet form for the production of pipes and fittings and included is a specially selected additive package to ensure: Enhanced processability Economical pipe production Excellent product consistency High temperature resistance Good impact strength
The pipe system will show high durability, good weldability, homogeneous joints, low tendency to incrustrations and fast and easy installation.
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高耐久性良好冲击性耐热易成型易焊接 | |||
| 颜色形状 | 灰色 | |||
| 成型方式 | 挤出管材挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 0.25 g/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 25 Mpa | ISO 527-2 | 50 mm/min |
拉伸延伸率 | |||
屈服(yld) | 13.5 % | ISO 527-2 | 50 mm/min |
弯曲模量 | 800 Mpa | ISO 178 | 2 mm/min |
拉伸模量 | 900 Mpa | ISO 527-2 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 2 kJ/m² | ISO 179/1eA | |
0℃ (32℉) | 3.5 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 20 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-20℃ (-4℉) | 40 kJ/m² | ISO 179/1eU | |
0℃ (32℉) | NB kJ/m² | ISO 179/1eU | |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 65 °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 45 °C | ISO 75-2 | |
维卡软化温度(Vicat) | 63 °C | ISO 306/B50 | |
线性膨胀系数(CLTE) | |||
- | 150 E-6/K | DIN 53752 | 0 °C-70 °C |
导热系数 | 0.24 W/(m K) | DIN 52612-1 |