SABIC® PPCOMPOUND G1520U
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC® PPcompound G1520U is a 20% short glass fiber reinforced polyporpylene and it is very resistant to UV. The base material is a PP homopolymer. The glass fibers are chemically coupled to the PP matrix.
Becasue of the unique and well balanced property profile the material is most suited for the building and construction market.
IMDS ID:794156176
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗紫外线均聚物填充增强 | |||
| 添加助剂 | 化学偶联剂紫外线稳定剂 | |||
| 增强填充 | 20% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.04 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 18 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.7 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 70 Mpa | ISO 527/1A | |
断裂(brk) | 80 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 3.5 % | ISO 527/1A | |
弯曲模量 | 4500 Mpa | ISO 178/1A | |
拉伸模量 | 4900 Mpa | ISO 527/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 160 °C | ISO 75/A | |
线性膨胀系数(CLTE) | |||
- | 60 E-6/K | ISO 11359-2 | -30 °C to 100 °C |