Total Energies Polypropylene PPC 10810
PP(聚丙烯)
道达尔能源(Total Energies)
产品描述
Polypropylene PPC 10810 is a high flow, very high impact heterophasic copolymer with a Melt Flow Index of 18 g/10min.
Polypropylene PPC 10810 is easy to process and has been developed for the injection moulding of automotive parts that require a very high impact resistance even at low temperature.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐低温冲击高流动 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 18 g/10min | ISO 1133 | |
堆积(视)密度 | 0.525 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 19 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
屈服(yld) | 6 % | ISO 527-2 | |
弯曲模量 | 950 Mpa | ISO 178 | |
拉伸模量 | 900 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6.5 kJ/m² | ISO 179 | |
-20℃ (-4℉) | 7.5 kJ/m² | ISO 179 | |
23℃ (73℉) | 50 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 8 kJ/m² | ISO 180 | |
23℃ (73℉) | 50 kJ/m² | ISO 180 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 85 °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | 50 °C | ISO 75 | 120°C per hour |
维卡软化温度(Vicat) | 135 °C | ISO 306 | 10N-50°C per hour |
维卡软化温度(Vicat) | 65 °C | ISO 306 | 50N-50°C per hour |
熔融温度(Tm) | 165 °C | ISO 3146 |