SABIC® PPCOMPOUND 3220H
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC® PPcompound 3220H is a 20% talc filled grade which is high heat stabilized, developed for under the bonnet applications. This material has been designed to combine a good performance profile with good processing.
SABIC® PPcompound 3220H is a designated automotive grade.
IMDS ID: 181948154
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 增强填充 | 20% 滑石粉 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.04 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 15 g/10min | ISO 1133 | |
收缩率 | |||
- | 1.2 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 36 Mpa | ISO 527/1A | |
断裂(brk) | 28 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 50 % | ISO 527/1A | |
弯曲模量 | 2700 Mpa | ISO 178/1A | |
拉伸模量 | 2700 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 2 kJ/m² | ISO 180/1A | |
0℃ (32℉) | 2.5 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 3 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 120 °C | ISO 75/B | |
线性膨胀系数(CLTE) | |||
- | 75 E-6/K | ISO 11359-2 | -30 °C to 100 °C |