SABIC® PPCOMPOUND 8671U
PP(聚丙烯)
沙特基础 (SABIC)
产品描述
SABIC® PPcompound 8671U is elastomer-modified mineral filled Polypropylene for automotive exterior applications. This material has been designed to combine a good stiffness and excellent impact performance with good processing and surface esthetics. SABIC®PPcompound 8671U is UV optimized
SABIC® PPcompound 8671 is a designated automotive grade.
IMDS ID: 982284895
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性良好冲击性增韧/冲击改性良好表面易成型抗紫外线填充增强 | |||
| 添加助剂 | 紫外线稳定剂抗冲击剂 | |||
| 增强填充 | 17% 矿物弹性体 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.022 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 27 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.6 % | Internal | 65x65x3.2mm, 24 hours after injection moulding |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527/1A | |
断裂(brk) | 15 Mpa | ISO 527/1A | |
拉伸延伸率 | |||
断裂(brk) | 60 % | ISO 527/1A | |
弯曲模量 | 1600 Mpa | ISO 178/1A | |
拉伸模量 | 1500 Mpa | ISO 527/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 10 kJ/m² | ISO 180/1A | |
0℃ (32℉) | 35 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 45 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 100 °C | ISO 75/B | |
线性膨胀系数(CLTE) | |||
- | 60 E-6/K | ISO 11359-2 | -30 °C to 100 °C |