Total Energies Polypropylene PPC 12712
PP(聚丙烯)
道达尔能源(Total Energies)
产品描述
Polypropylene PPC 12712 is a nucleated and controlled-rheology heterophasic copolymer with a very high Melt Flow Index of 70 g/10 min.
Polypropylene PPC 12712 is characterized by good stiffness and impact resistance as well as low shrinkage and low warpage. It has been formulated for excellent antistatic properties.
Polypropylene PPC 12712 has been developed for high speed injection moulding of thin walled packaging containers and household articles.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 良好的刚性良好冲击性低翘曲低收缩高流动 | |||
| 添加助剂 | 抗静电剂成核剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 0.905 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 70 g/10min | ISO 1133 | |
堆积(视)密度 | 0.525 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 25 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2 | |
弯曲模量 | 1200 Mpa | ISO 178 | |
拉伸模量 | 1300 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-20℃ (-4℉) | 4 kJ/m² | ISO 179 | |
23℃ (73℉) | 8 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
-20℃ (-4℉) | 3.5 kJ/m² | ISO 180 | |
23℃ (73℉) | 7 kJ/m² | ISO 180 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 84 R | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 100 °C | ISO 75 | 120°C per hour |
1.8 Mpa (264 psi)（18.6kg/cm²） | 55 °C | ISO 75 | 120°C per hour |
维卡软化温度(Vicat) | 140 °C | ISO 306 | 10N-50°C per hour |
维卡软化温度(Vicat) | 70 °C | ISO 306 | 50N-50°C per hour |
熔融温度(Tm) | 165 °C | ISO 3146 |