INSPIRE™ TF1305 SC
PP(聚丙烯)
盛禧奥(TRINSEO)
产品描述
Talc filled (16%), high impact PP Compound.
INSPIRE* TF1305 SC has been developed for covered interior automotive applications. Also designed for self-coloration (SC) in combination with PROMATCH* combi-masterbatches for uncovered applications with high demanding aesthetics, scratch resistance, and UV light stabilisation.
It is especially suitable for car interior applications requiring ductility, because of its high impact resistance, even at low temperature.
Applications:
Instrument panel retainer
Instrument panel trim
Mid console
Door panels
Door pockets
Interior trim
Trunk trim
基本信息
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 高冲击耐低温冲击良好表面耐刮擦抗紫外线填充增强 | |||
| 增强填充 | 16% 滑石粉 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.02 g/cm³ | ISO 1183 | |
熔体质量流动速率(MFR) | |||
230°C/2.16 kg | 9.5 g/10min | ISO 1133 | |
收缩率 | |||
- | 0.9~1.2 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 20 Mpa | ISO 527-2/50 | |
拉伸延伸率 | |||
断裂(brk) | 70 % | ISO 527-2/50 | |
弯曲模量 | 1850 Mpa | ISO 178 | 2.0 mm/min |
拉伸模量 | 1950 Mpa | ISO 527-2/1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
0℃ (32℉) | 8 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 15 kJ/m² | ISO 180/1A | |
仪器化落镖冲击能量 | |||
0℃ (32℉)总能量 | 70 J | ISO 6603-2 | Ductile Failure |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 110 °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 58 °C | ISO 75-2/A | Unannealed |
维卡软化温度(Vicat) | 135 °C | ISO 306 | A120 |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 85 E-6 cm/cm/℃ | ASTM D 696 |