Hostaform® C 2521
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Stiff-flowing grade for injection molding and extrusion
Chemical abbreviation according to ISO 1043-1: POM
Molding compound ISO 9988- POM-K, M-GNR, 01-002
POM copolymer
Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation.
Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470
Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm.
Ranges of applications: injection molding thick-walled, void-free molded parts; extrusion e.g. for boards and pipes.
FDA = Food and Drug Administration (USA)
FMVSS = Federal Motor Vehicle Safety Standard (USA)
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐热耐热老化抗氧化ESCR耐化学性耐碱耐燃油耐溶剂共聚物 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 2.5 cm³/10min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 2.8 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2.1 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
熔体密度 | 1.2 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 32 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2500 Mpa | ISO 178 | 23°C |
拉伸模量 | 2600 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 2300 Mpa | ISO 899-1 | |
1000h | 1100 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 8.5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 250 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 250 kJ/m² | ISO 179/1eU | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 144 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 101 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 151 °C | ISO 306 | 50°C/h 50N |
比热容 | 2210 J/kg-K | - | Melt |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |
导热系数 | 0.155 W/(m K) | - | Melt |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4 - | IEC 60250 | |
1MHz | 4 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 15 E-4 | IEC 60250 | |
1MHz | 50 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 |