Tenac™-C 3513
Tenac™-C 3513
POM(聚甲醛)
旭化成 (Asahi Kasei)
产品描述
Features: Copolymer; Creep Resistant; Fatigue Resistant; Good Toughness; High Impact Resistance; High Stiffness; High Strength; High Viscosity; UV Resistant; Weather Resistant
Uses: Automotive Interior Parts; Engineering Parts; Gears; Housings
基本信息
| 原厂资料 | 物性表-ASTM(英文) 物性表-ISO(英文) |
| 产品特性 | 高刚性耐疲劳高冲击高韧性抗蠕变抗紫外线耐候性高粘度共聚物 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.41 g/cm³
| ISO 1183 | |
比重 | 1.41 -
| ASTM D792 | |
熔体质量流动速率(MFR) | | | |
190℃/2.16 kg |
3 g/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
1.6~2 % | Internal | Flow / Right-angle |
纵向(Flow) |
1.6~2 % | Internal | para/perp to flow |
吸水率 | 0.2 %
| ASTM D570 | 23℃ 50% RH 24HR |
磨耗 | 14 mg
| ASTM D 1044 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
62 Mpa | ISO 527 | 23℃ 50% RH |
- |
62 Mpa | ASTM D 638 | |
拉伸延伸率 | | | |
断裂(brk) |
35 % | ASTM D638 | |
断裂(brk) |
40 % | ISO 527 | 23℃ 50% RH |
弯曲强度 | | | |
- |
88 Mpa | ASTM D790 | |
弯曲模量 | 2450 Mpa
| ASTM D790 | |
弯曲模量 | 2400 Mpa
| ISO 178 | 23℃ 50% RH |
拉伸模量 | 2500 Mpa
| ISO 527 | 23℃ 50% RH |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
23℃ (73℉) |
8 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | | | |
23℃ (73℉) |
96 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 78 M
| ASTM D 785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
158 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
153 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
110 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
93 °C | ISO 75 | |
线性膨胀系数(CLTE) | | | |
- |
100 E-6 mm/mm/℃ | ASTM D 696 | |
- |
100 E-6 mm/mm/℃ | ISO 11359 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+15~1.0E+16 Ohm-cm
| ASTM D257 | 23℃ 50% RH |
表面电阻率 | 1.0E+16~1.0E+17 Ohm
| ASTM D257 | 23℃ 50% RH |
绝缘强度 | 19 kV/mm
| ASTM D149 | |
耐电弧性 | 250 sec
| ASTM D495 | |