Hostaform® SlideX® C0313 XAP² ™
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
POM, Tribology
POM copolymer Injection molding grade with tribological modification for demanding applications that require prevention of audible noise caused by stick-slip phenomenon. Excellent tribological performance with low friction and low wear under various conditions of sliding against plastics and metals. Reduced emission grade. Emissions according to VDA 275 < 5 mg/kg
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988-1 :
POM-K | M-GNRS2 | 4-2 | - | POM copolymer
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨低摩擦低挥发VOC共聚物降噪音 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 13 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.6 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 60 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 11 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 40 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2550 Mpa | ISO 178 | 23°C |
拉伸模量 | 2700 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 140 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 150 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 140 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 93 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 151 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 130 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 130 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 170 °C | ISO 11357-1/-3 | 10°C/min |