LubriOne™ LB4200-5001 AR
POM(聚甲醛)
埃万特(原普立万)(Avient)
产品描述
LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨低摩擦共聚物 | |||
| 添加助剂 | 润滑剂 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.4 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 6~8 cm³/10min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
190℃/2.16 kg | 8~12 g/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.5~2.1 % | ISO 294-4 | |
横向(Across Flow) | 1.7~2.3 % | ISO 294-4 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 50 Mpa | ISO 527-2 | |
拉伸延伸率 | |||
断裂(brk) | 30 % | ISO 527-2 | |
弯曲强度 | |||
- | 60 Mpa | ISO 178 | |
弯曲模量 | 1800 Mpa | ISO 178 | |
拉伸模量 | 2000 Mpa | ISO 527-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 5 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | |||
- | NB kJ/m² | ISO 179 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 140 °C | ISO 75-2/B | Annealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 80 °C | ISO 75-2/A | Annealed |
维卡软化温度(Vicat) | 150 °C | ISO 306 | |
熔融温度(Tm) | 165~170 °C | Internal | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | - mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
相比漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 |