Hostaform® LX90Z XAP² ™
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Low emission, UV resistant grade, Metallic colors
Preliminary Data Sheet Hostaform® acetal copolymer grade LX90Z XAP2 ™ is UV stabilized material available in a range of molded in metallic colors generally for automotive interior applications. In addition, Hostaform® LX90Z XAP2 ™ has lower volatile emissions as required for some automotive interiors. Besides material, optimal finish for specialty metallic parts is dependent on proper drying, gate design, knit line locations, and special processing. Please contact Celanese Technical Service for assistance with your application. Low Emission Performance [VDA-275] <5 PPM
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 低挥发VOC抗紫外线共聚物 | |||
| 添加助剂 | 紫外线稳定剂脱模剂 | |||
| 颜色形状 | 粒状金属色 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.43 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 2.3 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.4 % | ISO 294-4, 2577 | |
吸水率 | 0.75 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 54 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-2/1A | 50mm/min |
弯曲强度 | |||
3.5%应变 | 67 Mpa | ISO 178 | |
弯曲模量 | 2900 Mpa | ISO 178 | 23°C |
拉伸模量 | 2700 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 147 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 90 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 90 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 100 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |