Celcon® UV90Z
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
UV resistant - automotive, general purpose grade, broad range of UV90Z colors
Celcon® UV90Z is an integrally colored nominal 9 melt flow rate based acetal copolymer material stabilized for use where ultraviolet radiation exposure is to be encountered. The material is formulated to prevent discoloration, fading, chalking and mechanical property change in severe ultraviolet exposure. This product is available in many colors formulated for the interior automotive market and other applications.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗紫外线共聚物 | |||
| 添加助剂 | 紫外线稳定剂脱模剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 8 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.9 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.7 % | ISO 294-4, 2577 | |
吸水率 | 0.75 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 64 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-2/1A | 50mm/min |
弯曲强度 | |||
3.5%应变 | 68 Mpa | ISO 178 | |
弯曲模量 | 2470 Mpa | ISO 178 | 23°C |
拉伸模量 | 2700 Mpa | ISO 527-2/1A | |
抗压强度 | 24 Mpa | ISO 604 | at 1% strain |
抗压强度 | 84 Mpa | ISO 604 | at 6% strain |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 102 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.7 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 155 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 91 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 161 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 120 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |