Celcon® GC25A
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
25% glass fibers, coupled for improved stiffness, standard grade
Celcon® acetal copolymer grade GC25A is a glass coupled formulation containing 25% reinforced fiber glass. This grade offers excellent strength, stiffness and heat distortion temperature with lower mold shrinkage, minimum thermal expansion, excellent dimensional stability and good moldability. Chemical abbreviation according to ISO 1043-1: POM
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热尺寸稳定易脱模共聚物填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 成型方式 | 注塑挤出 | |||
| 增强填充 | 25% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.58 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.2 % | ISO 294-4, 2577 | |
吸水率 | 0.8 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 106 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
断裂(brk) | 155 Mpa | ISO 178 | |
- | 160 Mpa | ISO 178 | 23°C |
弯曲模量 | 8700 Mpa | ISO 178 | 23°C |
拉伸模量 | 8600 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6.4 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 35 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 25 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 6 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 160 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 161 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 25 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 120 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |