Hostaform® C 9021 TF XAP² ™
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Tribological, low Emission
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNS, 2-2 POM copolymer Injection molding type, modified with PTFE; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation; for sliding combinations with very low coefficient of friction. Reduced emission grade. Emissions according to VDA 275 < 5 mg/kg Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: For sliding combinations with very low coefficient of friction. FMVSS = Federal Motor Vehicle Safety Standard (USA) Preliminary data sheet
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热耐热老化耐磨低摩擦低挥发VOC抗氧化耐化学性耐水解耐碱耐燃油耐溶剂共聚物填充增强 | |||
| 添加助剂 | 脱模剂润滑剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | PTFE | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.51 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 6 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.7 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 47 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 16 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2250 Mpa | ISO 178 | 23°C |
拉伸模量 | 2350 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 2000 Mpa | ISO 899-1 | |
1000h | 1150 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 60 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 60 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 120 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 98 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 145 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 3.7 - | IEC 60250 | |
1MHz | 3.7 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 20 E-4 | IEC 60250 | |
1MHz | 80 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 33 kV/mm | IEC 60243-1 |