Celcon® MC270-HM
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Mineral coupled for reduced warpage, high modulus, high flow
Celcon® MC270-HM is a high modulus, mineral coupled acetal copolymer. It utilizes a higher additive level to provide significant improvement in product stiffness and mold shrinkage and better warpage resistance than unfilled Celcon® M270. Celcon® MC270-HM is formulated to produce very flat, dimensionally stable parts.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性尺寸稳定低翘曲高流动共聚物 | |||
| 增强填充 | 矿物 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.57 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 1.5 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.3 % | ISO 294-4, 2577 | |
吸水率 | 0.75 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 45 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 5 % | ISO 527-2/1A | 50mm/min |
弯曲强度 | |||
- | 77 Mpa | ISO 178 | 23°C |
弯曲模量 | 3700 Mpa | ISO 178 | 23°C |
拉伸模量 | 3750 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 3.5 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 4.8 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.3 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 105 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 161 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 60 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 90 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |