Hostaform® C 2521 LS
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Stiff-flowing grade for injection molding and extrusion, UV resistant
POM copolymer Stiff-flowing type for injection molding and extrusion with high impact toughness and good tracking resistance over a high range of temperature; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. This grade has been specially stabilized to prevent discoloration and deterioration of mechanical properties from ultraviolet light exposure. The material is available in natural, black and colored. Burning rate ISO 3795 and FMVSS 302 < 75 mm/min for a thickness more than 1 mm. Ranges of applications: injection molding thick-walled, void-free molded parts; extrusion e.g. for boards and pipes. FMVSS = Federal Motor Vehicle Safety Standard (USA)
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击耐热耐热老化抗紫外线抗氧化ESCR耐化学性耐水解耐碱耐燃油耐溶剂共聚物 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 颜色形状 | 粒状本色黑色 | |||
| 成型方式 | 注塑挤出 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 2.5 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2.1 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
熔体密度 | 1.2 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 62 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 9 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 32 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2500 Mpa | ISO 178 | 23°C |
拉伸模量 | 2600 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 2300 Mpa | ISO 899-1 | |
1000h | 1100 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 7 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 8.5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 250 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 250 kJ/m² | ISO 179/1eU | Partial Break |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 144 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 101 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 151 °C | ISO 306 | 50°C/h 50N |
比热容 | 2210 J/kg-K | - | Melt |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |
导热系数 | 0.155 W/(m K) | - | Melt |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4 - | IEC 60250 | |
1MHz | 4 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 15 E-4 | IEC 60250 | |
1MHz | 50 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 |