Ultraform® W 2320 003 UNC Q600
Ultraform® W 2320 003 UNC Q600
POM(聚甲醛)
巴斯夫 (BASF)
产品描述
Ultraform W 2320 003 UNC Q600 is a very easy flowing and rapidly solidifying injection molding POM grade for use where processing is extremely difficult but mechanical properties are lower. Contains a mold release agent.
Applications
Typical applications include thin walled parts.
基本信息
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) |
| 产品特性 | 易脱模高流动 |
| 添加助剂 | 脱模剂 |
| 成型方式 | 注塑 |
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
密度 | 1.4 g/cm³
| ISO 1183 | |
比重 | 1.4 -
| ASTM D792 | |
熔体体积流动速率(MVR) | | | |
190℃/2.16 kg |
25 cm³/10min | ISO 1133 | |
收缩率 | | | |
纵向(Flow) |
2 % | ISO 294-4 | |
横向(Across Flow) |
2.1 % | ISO 294-4 | |
- |
1.9 % | Internal | |
吸水率 | 0.2 %
| ASTM D570 | 50% RH |
吸水率 | 0.8 %
| ASTM D570 | Saturation |
吸水率 | 0.2 %
| ISO 62 | 50% RH |
吸水率 | 0.8 %
| ISO 62 | Saturation |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
65 Mpa | ASTM D638 | 23℃ |
屈服(yld) |
93 Mpa | ISO 527 | -40℃ |
屈服(yld) |
65 Mpa | ISO 527 | 23℃ |
屈服(yld) |
33 Mpa | ISO 527 | 80℃ |
拉伸延伸率 | | | |
屈服(yld) |
7.5 % | ASTM D638 | 23℃ |
屈服(yld) |
7.5 % | ISO 527 | 23℃ |
标称断裂伸长率 |
24 % | ISO 527 | 23℃ |
弯曲模量 | 2760 Mpa
| ASTM D790 | 23℃ |
拉伸模量 | 2800 Mpa
| ISO 527 | 23℃ |
拉伸蠕变模量 | | | |
1h |
2100 Mpa | ISO 899 | |
1000h |
1350 Mpa | ISO 899 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | | | |
-30℃ (-22℉) |
4 kJ/m² | ISO 179 | |
23℃ (73℉) |
5 kJ/m² | ISO 179 | |
简支梁无缺口(Charpy Unnotched) | | | |
-30℃ (-22℉) |
150 kJ/m² | ISO 179 | |
23℃ (73℉) |
150 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | | | |
-40℃ (-40℉) |
44.8 J/m | ASTM D256 | |
23℃ (73℉) |
55 J/m | ASTM D256 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
154 °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
156 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
99 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
100 °C | ISO 75 | |
相对温度指数(RTI) | | | |
冲击w/impact,1.5/1.6 mm |
90 °C | UL 746B | |
冲击w/impact,3.0/3.2 mm |
90 °C | UL 746B | |
电气Elec,1.5/1.6 mm |
105 °C | UL 746B | |
电气Elec,3.0/3.2 mm |
105 °C | UL 746B | |
强度w/o impact,1.5/1.6 mm |
90 °C | UL 746B | |
强度w/o impact,3.0/3.2 mm |
105 °C | UL 746B | |
线性膨胀系数(CLTE) | | | |
纵向(Flow) |
110 E-6/°C | Internal | |
- |
60 E-6/°C | ASTM D E831 | |
熔融温度(Tm) | 167 °C
| ASTM D3418 | |
熔融温度(Tm) | 167 °C
| ISO 3146 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | | | |
HB |
1.5 mm | UL94 | |
HB |
3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm
| ASTM D257 | 1.5 mm |
体积电阻率 | 1.0E+13 Ohm-cm
| IEC 60093 | |
表面电阻率 | 1.0E+13 Ohm
| ASTM D257 | 1.5 mm |
表面电阻率 | 1.0E+13 Ohm
| IEC 60093 | |
介电常数(DK) | | | |
100Hz |
3.8 - | IEC 60250 | |
1MHz |
3.8 - | IEC 60250 | |
耗散因数(DF) | | | |
100Hz |
10 E-4 | IEC 60250 | |
1MHz |
50 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | | | |
- |
600 V | IEC 60112 | |
绝缘强度 | 40 kV/mm
| IEC 60243-1 | |