Hostaform® C 52021 LS
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Injection molding grade with extremely high flow
POM copolymer Extremely easy flowing Injection molding type for very thin-walled precision molded parts with unfavourite flow-path-wall thickness relation; permits processing at reduced temperature and also shorter cycle times; for mechanical lower requirements; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high esistance to thermal and oxidative degradation. With UV Additives Ranges of applications: For very thin-walled precision molded parts with unfavourite flow-path-wall thickness relation; permits processing at reduced temperature and also shorter cycle times.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热耐热老化短周期成型抗紫外线抗氧化耐化学性耐水解耐碱耐燃油耐溶剂高流动共聚物 | |||
| 添加助剂 | 紫外线稳定剂脱模剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 39 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 1.9 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
熔体密度 | 1.2 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 65 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 15 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2800 Mpa | ISO 178 | 23°C |
拉伸模量 | 3000 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 2500 Mpa | ISO 899-1 | |
1000h | 1300 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 5 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 150 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 150 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 148 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 106 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 151 °C | ISO 306 | 50°C/h 50N |
比热容 | 2060 J/kg-K | - | Melt |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |
导热系数 | 0.19 W/(m K) | - | Melt |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4 - | IEC 60250 | |
1MHz | 4 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 30 E-4 | IEC 60250 | |
1MHz | 50 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 |