Celcon® M90SW
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
Low wear, low noise for high load, low speed applications.
Celcon M90SW is a low wear grade designed for gears and other low wear applications, especially where reducing noise and wear against the same mating surface is important. This grade may be preferred in high load-low velocity applications. Celcon® M90SW is an option where silicone or PTFE based wear resistant products are not acceptable. Please also see Hostaform® C 9021 SW.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐磨低摩擦共聚物降噪音 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 8 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.6 % | ISO 294-4, 2577 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 49 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 2560 Mpa | ISO 178 | 23°C |
拉伸模量 | 2600 Mpa | ISO 527-2/1A | |
抗压强度 | 21 Mpa | ISO 604 | at 1% strain |
抗压强度 | 72 Mpa | ISO 604 | at 6% strain |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 5 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 90 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 105 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 5.4 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 90 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 161 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 100 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 100 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |