Hostaform® C 13031 XAP
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
high stiffness
Polyacetal copolymer, reduced emission Easy flowing Injection molding type like C 13021 XAP, but with higher strength, rigidity and hardness over the entire permissible temperature range for HOSTAFORM; good chemical resistance to solvents, fuel and strong alkalis as well as good hydrolysis resistance; high resistance to thermal and oxidative degradation. Emissions according to VDA 275 < 10 ppm (natural and colored grades) Monomers and additives are listed in EU-Regulation (EU) 10/2011 FDA compliant according to 21 CFR 177.2470 Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm. Ranges of applications: For molded parts with higher requirements to strength, rigidity und hardness, ranges of applications with fuel contact.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热耐热老化抗氧化耐化学性耐水解耐碱耐燃油耐溶剂高流动共聚物 | |||
| 法规认证 | EU Food Contact(2011/10/EC)(欧盟食品级)FDA(食品药品监督管理局) | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.41 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 12 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.8 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 68 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 8 % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 28 % | ISO 527-2/1A | 50mm/min |
弯曲模量 | 3000 Mpa | ISO 178 | 23°C |
拉伸模量 | 3050 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 2750 Mpa | ISO 899-1 | |
1000h | 1450 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 6 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 6.7 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 200 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 200 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 156 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 107 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 158 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 110 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 170 °C | ISO 11357-1/-3 | 10°C/min |
导热系数 | 0.155 W/(m K) | - | Melt |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4 - | IEC 60250 | |
1MHz | 4 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 20 E-4 | IEC 60250 | |
1MHz | 50 E-4 | IEC 60250 | |
相比漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 |