LNP™ THERMOCOMP™ KF002L
POM(聚甲醛)
沙特基础 (SABIC)
产品描述
LNP THERMOCOMP KF002L is a compound based on Acetal Homopolymer resin containing 10% Glass Fiber. Added features of this material include: Low Extractible.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 均聚物填充增强 | |||
| 增强填充 | 10% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.49 g/cm³ | ISO 1183 | |
密度 | 1.49 g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | 1.7 % | ISO 294 | flow, 24 hrs |
纵向(Flow) | 1.6~1.8 % | ASTM D 955 | flow, 24 hrs |
横向(Across Flow) | 1.5~1.7 % | ASTM D 955 | xflow, 24 hr |
横向(Across Flow) | 1.6 % | ISO 294 | xflow, 24 hr |
吸湿率 | 0.2 % | ASTM D 570 | 50% RH, 24 hrs |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 66 Mpa | ASTM D638 | |
屈服(yld) | 65 Mpa | ISO 527 | |
断裂(brk) | 63 Mpa | ISO 527 | |
断裂(brk) | 63 Mpa | ASTM D638 | |
拉伸延伸率 | |||
屈服(yld) | 2.2 % | ASTM D638 | |
屈服(yld) | 2.1 % | ISO 527 | |
断裂(brk) | 3.4 % | ASTM D638 | |
断裂(brk) | 3.2 % | ISO 527 | |
弯曲强度 | |||
- | 103 Mpa | ASTM D790 | |
- | 105 Mpa | ISO 178 | |
弯曲模量 | 4820 Mpa | ASTM D790 | |
弯曲模量 | 4400 Mpa | ISO 178 | |
拉伸模量 | 6200 Mpa | ASTM D638 | 50 mm/min |
拉伸模量 | 5600 Mpa | ISO 527 | 1 mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 42 J/m | ASTM D256 | |
23℃ (73℉) | 4 kJ/m² | ISO 180/1A | 80*10*4 |
悬臂梁无缺口(Izod Unnotched) | |||
23℃ (73℉) | 384 J/m | ASTM D4812 | |
23℃ (73℉) | 26 kJ/m² | ISO 180/1U | 80*10*4 |
仪器化落镖冲击能量 | |||
23℃ (73℉)峰值 | 6 J | ASTM D3763 | |
多轴冲击 | 2 J | ISO 6603 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 162 °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | 162 °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | 155 °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | 148 °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 10.8 E-6/°C | ASTM E831 | -40°C to 40°C, flow |
纵向(Flow) | 112 E-6/°C | ISO 11359-2 | -40°C to 40°C, flow |
横向(Across Flow) | 5.4 E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
横向(Across Flow) | 60.5 E-6/°C | ISO 11359-2 | -40°C to 40°C, xflow |