Celcon® GC25TF
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
25% glass fibers, coupled for improved stiffness, high strength, fuel resistant, and high flow for thin parts
Celcon® GC25TF is a 25% glass coupled acetal copolymer formulated for higher flow in thin walled and small parts. Celcon GC25TF is also exceptionally resistant to fuel. It offers excellent resistance to transportation fuels especially oxygenated fuels. Chemical abbreviation according to ISO 1043-1: POM
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐燃油高流动共聚物填充增强 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 25% 玻纤 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.58 g/cm³ | ISO 1183 | |
吸水率 | 0.8 % | ISO 62 | 23°C-sat |
吸湿率 | 0.2 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 120 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-2/1A | 50mm/min |
断裂(brk) | 2 % | ISO 527-2/1A | 5mm/min |
弯曲模量 | 8710 Mpa | ISO 178 | 23°C |
拉伸模量 | 8720 Mpa | ISO 527-2/1A | |
抗压强度 | 69 Mpa | ISO 604 | at 1% strain |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 6.4 kJ/m² | ISO 179/1eA | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 6.4 kJ/m² | ISO 180/1A | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 162 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 161 °C | ISO 306 | 50°C/h 50N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 30 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 100 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |