Hostaform® S 9364 TM01 XAP² ™
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
highly impact modified grade with low emission
Preliminary Data Sheet Hostaform® acetal copolymer grade S 9364 TM01 XAP2 ™ is highly impact modified grade for demanding applications. Hostaform® S 9364 TM01 XAP2 ™ provides a significant improvement in impact strength and flexibility over standard impact modified grades such as Hostaform® S 9063 and S 9064, and also exhibits exceptional low emission performance meeting or exceeding the requirements of many automotive markets. Chemical abbreviation according to ISO 1043-1: POM-HI
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击高韧性低挥发VOC共聚物 | |||
| 添加助剂 | 抗冲击剂脱模剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.36 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 4 cm³/10min | ISO 1133 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 43 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 13 % | ISO 527-2/1A | 50mm/min |
拉伸模量 | 1700 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 15 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 77 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |