Hostaform® S 4000P CT
POM(聚甲醛)
塞拉尼斯(Celanese)
产品描述
POM, Impact Modified, High Flow
Chemical abbreviation according to ISO 1043-1: POM-HI POM copolymer, modified Hostaform® S 4000P CT is an impact-modified acetal copolymer with high flowability for demanding injection molding applications. Hostaform® S 4000P CT has a significantly higher MVR compared to Hostaform® S 27064, with comparable mechanical properties, and is non-hygroscopic in nature. It is recommended for long flow length and/or thin-walled part geometries.
基本信息
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高冲击高韧性高流动共聚物 | |||
| 添加助剂 | 抗冲击剂脱模剂增塑剂 | |||
| 成型方式 | 注塑 | |||
技术参数
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.37 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 39 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 2 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.9 % | ISO 294-4, 2577 | |
吸水率 | 0.65 % | ISO 62 | 23°C-sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 38 Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | |||
屈服(yld) | 12 % | ISO 527-2/1A | 50mm/min |
拉伸模量 | 1600 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 8.5 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |